1060 Aluminum Coil

1060 aluminum alloy is formed by adding a small amount of copper to pure aluminum. It has excellent forming properties, high corrosion resistance, good weldability and electrical conductivity.

1060 is widely used in products that do not require high strength, such as chemical instruments, thin plate processing parts, deep-drawing or spinning concave containers, welded parts, heat exchangers, watch faces and dials, nameplates, kitchen utensils, decorations, and reflective appliances.

1060 Pure Aluminum (Standard: GB/T3190-2008) Industrial pure aluminum has the characteristics of high plasticity, good corrosion resistance, good electrical and thermal conductivity, but low strength, can not be strengthened by heat treatment, poor workability, and can be subject to contact welding and gas welding.

1060 Aluminum Coil
Standard	JIS, AiSi, ASTM, GB, DIN, EN etc
Grade	1000 Series,2000,3000 Series,4000Series,5000Series,6000Series,7000Series,8000Series,,9000Series
Surface	Coated, Embossed,Brushed, polished, Anodized,etc
OEM service	Perforated, Cutting special size, Doing flatness, Surface treatment,etc
Delivery Time	Within 3 days for our stock size,15-20days for our production
Application	Construction filed, Ships building industry, Decoration, Industry,Manufacture,Machinery and hardware fields, etc
Sample	Free and available
Package	Export standard package: bundled wooden box, suit for all kinds of transport,or be required

Available Size Range

Dimension	Range
Thickness	0.2 ~ 6.0 mm
Width	600 ~ 2,600 mm

* The thickness can be up to 10mm for coil stock (mother coil for cold rolling).
- Standard Width and Length: 1000mm, 1250mm, 1500mm, 1219mm, 1524mm
- Surface Finish: Mill finish, unless otherwise specified
- Surface Protection:
Without paper interleaved for all aluminum coils
With PE/PVC filming on main side (if specified)

Chemical Properties of Frequently-used :

Grade	SI	FE	CU	MN	MG	CR	NI	ZN	AL
1050	0.25	0.4	0.05	0.05	0.05			0.05	99.5
1060	0.25	0.35	0.05	0.03	0.03			0.05	99.6
1070	0.2	0.25	0.04	0.Q3	0.03			0.04	99.7
1100	Si+Fe:0.95		0.05-0.2	0.05			0.1		99
1200	Si+Fe:1.00		0.05	0.05			0.1	0.05	99
1235	Si+Fe:0.65		0.05	0.05	0.05		0.1	0.06	99.35
3003	0.6	0.7	0.05-0.2	1.0-1.5				0.1	remains
3004	0.3	0.7	0.25	1.0-1.5	0.8-1.3			0.25	remains
3005	0.6	0.7	0.25	1.0-1.5	0.20-0.6	0.1		0.25	remains
3105	0.6	0.7	0.3	0.30-0.8	0.20-0.8	0.2		0.4	remains
3A21	0.6	0.7	0.2	.0-1.6	0.05			0.1	remains
5005	0.3	0.7	0.2	0.2	0.50-1.1	0.1		0.25	remains
5052	0.25	0.4	0.1	0.1	2.2-2.8	0.15-0.35		0.1	remains
5083	0.4	0.4	0.1	0.40-1.0	4.0-4.9	0.05-0.25		0.25	remains
5154	0.25	0.4	0.1	0.1	3.1 -3.9	0.15-0.35		0.2	remains
5182	0.2	0.35	0.15	0.20-0.50	4.0-5.0	o.i		0.25	remains
5251	0.4	0.5	0.15	0.1-Q.5	1.7-2.4	0.15		0.15	remains
5754	0.4	0.4	0.1	0.5	2.6-3.6	0.3		0.2	remains